Effect of Cationic/Anionic Diffusion Dominated Passive Film Growth on Tribocorrosion

Abstract

Tribocorrosion behaviours of nickel (Ni) and niobium (Nb) in sodium sulfate (Na2SO4) solution under potentiodynamic and potentiostatic conditions were studied. Under the potentiodynamic condition, the passivation was early broken, accompanied by a sharp increase in frictional coefficient on Nb. The current was more fluctuant, and larger material loss appeared at the higher potential in the potentiostatic condition. However, these phenomena did not occur for Ni, and it even showed lower material loss at the higher potential in the potentiostatic tribocorrosion test. The differences in tribocorrosion behaviour had a close relationship to the passive film growth mechanism, which decided the passive film/metal interface structure. Nb with anionic diffusion dominated mechanism in passive growth would cause the accumulation of oxygen vacancies at the passive film/metal interface. This may weaken the adhesion between the metal and the passive film. However, with the cationic diffusion dominated passive film growth on Ni, cation vacancies concentrated at the passive film/tribo-film interface, and this did not affect the adhesion between metal and passive film. Ni or other passive elements with the cationic diffusion-dominated mechanism in passive film growth were recommended as the alloying element for improving the tribocorrosion resistance of alloys.

Keywords

• tribocorrosion
• passivation
• wear
• corrosion
• interface