Effects of modified elastin-collagen matrix on the thermal and mechanical properties of Poly (lactic acid)

Abstract

Poly (lactic acid) (PLA) has distinctive characteristics, including biodegradability, biocompatibility, thermal process ability, high transparency and good film-forming ability. However, PLA has some poor properties that limit its wide applicability. These properties include a low crystallization rate, poor thermal stability, and high brittleness. The main objective of this research was to investigate the effect of a modified elastin-collagen (m-ELA-COLL) matrix on the properties of PLA. The ELA-COLL matrix was extracted from broiler skin waste and modified by grafting using lactic acid monomer to facilitate compatibility with PLA. The extracted and modified ELA-COLL matrix was investigated using FTIR, and α-helix and β-sheet structures were confirmed in both cases (pre- and post-modifications). Modified elastin-collagen dispersed Poly (lactic acid) (PLA-m-ELA-COLL) blend films were prepared using the solution casting method and characterized using DSC and UTM. The effect of m-ELA-COLL as a nucleating agent resulted in the degree of crystallinity improvement of 58.8% with 10 wt% m-ELA/COLL loading, and the elongation at break was improved by 161.3% for PLA-40%-m-ELA-COLL with a tensile strength of 33.75 MPa. The results obtained revealed that the biofilms can be considered as a good candidate to be studied further in the packaging industry.

Keywords

• Biofilms
• Crystallinity
• Mechanical properties
• Modified elastin-collagen matrix
• Poly (lactic acid)