Boletín de la Sociedad Española de Cerámica y Vidrio (Feb 2009)

Cerámicas nanoestructuradas de óxido anódico de aluminio. Diseño de célula electroquímica, cinética de crecimiento y caracterización

  • Ferrer Giménez, C.,
  • Rayón Encinas, E.

Journal volume & issue
Vol. 48, no. 1
pp. 25 – 32

Abstract

Read online

An electrochemical cell design has been presented to grow anodic aluminium oxide, Al<sub>2</sub>O<sub>3</sub>, with nanoporous structures in a 10 cm diameter wafers. The electrochemical kinetics showed four steps of growth. The membranes growth submerged in 0.3 M (COOH)<sub>2</sub> acid and in H<sub>3</sub>PO<sub>4</sub> acid. The electrochemical anodization revealed a nanoporous morphology. Pores diameters, D<sub>P</sub>=45 nm in oxalic acid and D<sub>P</sub>=240 nm in phosphoric acid were obtained.<br><br>Se presenta un diseño de célula electroquímica para formar cerámicas nanoporosas de óxido anódico de aluminio, Al<sub>2</sub>O<sub>3</sub>, en obleas circulares de 10 cm de diámetro. Las cinéticas electroquímicas revelaron cuatro etapas en el crecimiento de la membranas mientras que la influencia de los factores de anodización fueron estudiados. Las imágenes por microscopía SEM y AFM mostraron que las cerámicas obtenidas bajo anodización en ácido (COOH)<sub>2</sub> 0.3M y en ácido H<sub>3</sub>PO<sub>4</sub> diluido al 10% presentaron una morfología nanoporosa con diámetros de poro, D<sub>P</sub>=45 nm para el oxálico y un D<sub>P</sub>=240 nm para el fosfórico.

Keywords