Cerâmica (Sep 2008)
Stability of crack propagation during bending tests on brittle materials Estabilidade de propagação de trinca durante testes de flexão em materiais frágeis
Abstract
Applications of ceramic materials usually involve thermal stresses that can reduce their lifetime considerably. One of the most relevant mechanical properties for evaluating thermal shock damage resistance is the energy of fracture. In order to obtain this property, a stable crack growth regimen must be achieved throughout the test. In this paper, three-point bending tests are analyzed to determine how machine stiffness influences load point displacement rates. Understanding the differences between recorded and adjusted displacement rates is important in determining the stability of crack growth. This statement is corroborated by experimental data on sintered high-alumina, low-cement refractory castables.Em geral, a aplicação de materiais cerâmicos envolve a ocorrência de tensões térmicas que podem encurtar consideravelmente o seu tempo de operação. Uma das propriedades mecânicas mais relevantes para a avaliação da resistência ao dano por choque térmico é a energia de fratura. Para se obter isso, é necessário que ao longo do teste se atinja uma condição de crescimento estável de trinca. Neste artigo, analisa-se o teste de flexão em três pontos para se determinar como a rigidez da máquina de ensaio influencia a taxa de deslocamento do ponto de aplicação de carga. Para o estabelecimento da estabilidade do crescimento de uma trinca, é importante a compreensão das diferenças entre as taxas de deslocamento registradas e as ajustadas. Esta afirmação é corroborada por dados experimentais obtidos com concretos refratários de alta alumina e baixo cimento.
Keywords