Role of Post-Exposure Time in Co(II) Sorption of Higher Concentrations on Electron Irradiated Sheep Wool

Abstract

Sorption of Co(II) was investigated on natural as well as accelerated electron beam modified sheep wool involving low and high concentrations up to 200 mmol·dm−3. The sorption experiments confirmed the dependence of the sorption capacity not only on sorbate concentration and absorbed dose of energy, but also on post-exposure time. Post-exposure heating to accelerate transformation of the wool structure was of no effect on the sorption comparing with a simple storage for a period of 100 days. Under all tested conditions, the sorption maximum was measured for Co(II) concentration of 125 mmol·dm−3 and that was assigned to form a Co(II) complex with keratin. This assumption was tested on visible spectra of mixed solutions of Arginine and Co(II) to be a simplified model of Co(II) interaction with keratin. The sorption decrease is associated with generation of cross links between macro-chains through ligands of the Co-complex. The nodal points are a hindrance to diffusion of next ions into the fibers. Also, pH variations of aqueous extracts from the wool samples depending on absorbed dose and post-exposure time indicate complexity of the structural transformation being specific for each dose applied.

Keywords

• sheep wool
• electron beam irradiation
• cobalt sorption
• post-exposure time
• Co-complex