Effect of Rare Earth Cerium Addition on Microstructures and Mechanical Properties of Low Carbon High Manganese Steels

Abstract

Low carbon high manganese steels with different Ce contents were melted in medium frequency vacuum induction furnace. The microstructures and mechanical properties of steels were studied by OM, SEM, EDS and mechanical property testing. The results showed that the microstructures of experimental steels were refined remarkably, inclusions distributed more finely and uniformly, the tensile strength and impact toughness of tested steels both improved greatly after the addition of Ce. Thermodynamic calculation results demonstrated that Ce contained inclusions were Ce2O3 and Ce3S4, which agreed well with the results observed by SEM and EDS. By analysis of two-dimensional lattice disregistry, it was shown that the lattice misfit parameter between δ-Fe and Ce2O3, Ce3S4 are less than 6 %, which indicated that Ce2O3 and Ce3S4 could effectively act as the heterogeneous nuclei of initial δ-Fe. Therefore, the microstructures were refined significantly and the mechanical properties were improved correspondingly in Ce-added low carbon high manganese steels.

Keywords

• low carbon high manganese steels
• ce
• inclusion
• microstructures
• mechanical properties
• 81