Experimental investigation of high He/dpa microstructural effects in neutron irradiated B-alloyed Eurofer97 steel by means of small angle neutron scattering (SANS) and electron microscopy

Abstract

High He/dpa microstructural effects have been investigated, by means of small-angle neutron scattering (SANS) and transmission electron microscopy (TEM), in B-alloyed ferritic/martensitic steel Eurofer97-1 (0.12 C, 9 Cr, 0.2V, 1.08W wt%, B contents variable between 10 and 1000ppm), neutron irradiated at the High Flux Reactor of the JRC-Petten at temperatures between 250 °C and 450 °C, up do a dose level of 16 dpa. Under these irradiation parameters, B activation is expected to produce corresponding helium contents variable between 80 and 5600appm, with helium bubble distributions relevant for the technological applications. The SANS measurements were carried out under magnetic field to separate nuclear and magnetic SANS components; a reference, un-irradiated sample was also measured to evaluate as accurately as possible the genuine effect of the irradiation on the microstructure. Increasing the estimated helium content from 400 to 5600appm, the analysis of the SANS cross-sections yields an increase in the volume fraction, attributed to helium bubbles, of almost one order of magnitude (from 0.007 to 0.038); furthermore, the difference between nuclear and magnetic SANS components is strongly reduced. These results are discussed in correlation with TEM observations of the same samples and are tentatively attributed to the effect of drastic microstructural changes in Eurofer97-1 for high He/dpa ratio values, possibly relating to the dissolution of large B-carbides due to transmutation reactions.

Keywords

• Helium effects
• Neutron irradiation
• Small angle neutron scattering
• Electron microscopy