Boletín de la Sociedad Española de Cerámica y Vidrio (Feb 2002)
Efecto de los parámetros de procesamiento sobre las características cristalinas de la solución sólida Y(Co<sub>x</sub>Mn<sub>1-x</sub>)O<sub>3</sub>, x=0.6, 0.7
Abstract
The preparation and crystalline features of perovskite solid solution Y(CoxMn1-x)O3, x=0.6, 0.7, belonging to the Co-rich region of the pseudobinary system YMnO3-YCoO3 have been studied. Dilatometric essays performed under different atmospheres have been carried out for determining the best conditions to obtain single-phase samples. Influence of the thermal cycle and of the sintering density on the appearance of secondary phases has been also established. Firing under O2 atmosphere favours the formation of the pure perovskite. The cooling rate plays an important role for inhibiting the formation of secondary phases. All the crystalline parameters depend ultimately on the final density of the polycrystalline bodies.Se han estudiado la preparación y las características cristalinas de la solución sólida Y(CoxMn1-x)O3, x=0.6, 0.7, con estructura de tipo perovsquita, perteneciente a la región rica en Co del sistema seudobinario YMnO3-YCoO3. Se han llevado a cabo ensayos dilatométricos bajo diferentes atmósferas para determinar las mejores condiciones para obtener cerámicas monofásicas. Se ha establecido igualmente la influencia del ciclo térmico y de la densidad de sinterizado sobre la aparición de fases secundarias. La sinterización en oxígeno favorece la formación de la perovsquita pura. La velocidad de enfriamiento juega un importante papel sobre la inhibición de la formación de fases secundarias. Todos los parámetros cristalinos dependen finalmente de la densidad final de los materiales cerámicos.