Abstract

In this work, a novel AaBAb-type triblock polycarboxylate superplasticizers (PCEs) with well defined molecular structures were designed and synthesized, firstly, by reversible addition-fragmentation chain transfer (RAFT) polymerization, to explore the structure–property relationship PCEs in the β-hemihydrate gypsum (β-HH) system. Three PCEs with the same molecular weight and different structure were obtained by changing the feed ratio of the RAFT agent, initiator, and monomer. The effect of the chemical structure of PCEs on their dispersing property and water reduction capacity were assessed in gypsum by measuring the flowability of pastes and the adsorption ability of PCEs on gypsum. Results showed that among three PCEs, when the monomer ratio is 5:1 and a:b = 1:1, PCE-1 exhibited a higher working efficiency, verifying the contribution of regulating structural parameters to the improvement in performances of gypsum paste, because PCE-1 showed the strongest binding capacity with calcium ions due to the relatively equal amount of carboxyl groups at both ends. The AaBAb-type PCEs provide a special advantage over the conventional comb polymer to understand the relation between the structure and property of PCEs, and a direction for further development of PCEs of high performance.

Keywords

• gypsum
• hemihydrate
• triblock
• polycarboxylate
• superplasticizer
• dispersion