Evolution of the Surface Wettability of PET Polymer upon Treatment with an Atmospheric-Pressure Plasma Jet

Abstract

A useful technique for pre-treatment of polymers for improved biocompatibility is surface activation. A method for achieving optimal wettability at a minimal thermal load and unwanted modifications of the polymer properties is elaborated in this paper. Samples of polyethylene terephthalate polymer were exposed to an atmospheric-pressure plasma jet created by a high-impedance low-frequency discharge in wet argon. Different treatment times and distances from the end of the glowing discharge enabled detailed investigation of the evolution of surface activation. A rather fast saturation of the surface wettability over the area of the order of cm2 was observed upon direct treatment with the glowing discharge. At a distance of few mm from the glowing discharge, the activation was already two orders of magnitude lower. Further increase of the distance resulted in negligible surface effects. In the cases of a rapid activation, very sharp interphase between the activated and unaffected surface was observed and explained by peculiarities of high-impedance discharges sustained in argon with the presence of impurities of water vapor. Results obtained by X-ray photoelectron spectroscopy confirmed that the activation was a consequence of functionalization with oxygen functional groups.

Keywords

• atmospheric-pressure plasma jet
• polymer
• surface patterns
• wettability mapping
• xps mapping