Investigation on the Mechanical Properties and Microstructure of Eco-friendly Mortar Containing WGP at Elevated Temperature

Abstract

Abstract The properties of mortars containing waste glass powder (WGP) as a cement substitute for sustainable construction at various high temperatures were investigated. For this purpose, specimens from four mixtures with WGP at various percentage levels of 0, 5, 10 and 15% were prepared and exposed to the specified temperatures. After that, the compressive and flexural strength were determined at high temperatures. The mass loss was also measured by weighing the samples before and after exposing to the high temperatures. The microstructure of mortars was analyzed by petrographic examination. Based on the obtained results, incorporation of WGP as partial replacement of cement could improve strength characteristics of the mortars at the elevated temperatures up to 17%. Also, the optimum ratio of cement replacement level was found to be 10%. In addition, the petrographic images of the mortars showed that at the same time with the strength loss of specimens, the red discoloration of WGP occurred that is attributed to the oxidation of iron compounds that starts at temperatures above 200 °C.

Keywords

• eco-friendly mortar
• waste glass powder
• mechanical properties
• petrography