The heat-aging process, a practical aging technology that not only improves the comprehensive performance of Al alloys but also reflects the requirements of short processes, has an extremely practical significance. The effects of the heating rate and termination temperature on the “heat-aging” behavior of a spray-deposited AlZnMgCu alloy hot-extruded plate were investigated using hardness, electrical conductivity, room-temperature tensile strength, exfoliation corrosion experiments, and transmission electron microscopy microstructure (TEM) observation. The results show that as the termination temperature increases, the hardness of the spray-deposited AlZnMgCu alloy first increases to a peak and then rapidly decreases, while the electrical conductivity continues to increase. The increase in the heating rate improves the peak hardness corresponding to the termination temperature. The heat treatment process of heating at a speed of 20 °C/h to 200 °C after the spray deposition has similar mechanical and corrosion resistance properties to the RRA process and can effectively reduce the heating time from 40 h to 8 h, thus establishing a heat treatment process for spray-deposited AlZnMgCu alloy extruded plate with high aging efficiency.