Influence of Al Content on the Inclusion-Microstructure Relationship in the Heat-Affected Zone of a Steel Plate with Mg Deoxidation after High-Heat-Input Welding

Abstract

The effects of Al content on inclusions, microstructures, and heat-affected zone (HAZ) toughness in a steel plate with Mg deoxidation have been investigated by using simulated high-heat-input welding and an automated feature system. The studies indicated that the main kind of oxysulfide complex inclusions in two steels without and with Al addition were both MgO-MnS. The number densities and mean sizes of inclusions were 96.65 mm−2 and 3.47 μm, 95.03 mm−2 and 2.03 μm, respectively. The morphologies of MgO-MnS complex inclusions in steel were changed obviously with the addition of Al. When containing 0.001 wt.% Al, they consisted of a central single MgO particle and outside, the MnS phase. When containing 0.020 wt.% Al, they comprised several small MgO particles entrapped by the MnS phase. Because the former could nucleate intragranular acicular ferrites (IAFs) and the latter was non-nucleant, the main intragranular microstructures in HAZs were ductile IAFs and brittle ferrite side plates (FSPs), respectively. Therefore, HAZ toughness of the steel plate without Al addition after high-heat-input welding of 400 kJ/cm was significantly better than that of the steel plate with Al addition.

Keywords

• Mg deoxidation
• inclusions
• Al addition
• high-heat-input welding
• heat-affected zone
• toughness