<em>Nelumbo nucifera</em> Seed–Derived Nitrogen-Doped Hierarchically Porous Carbons as Electrode Materials for High-Performance Supercapacitors

Abstract

Biomass-derived activated carbon materials with hierarchically nanoporous structures containing nitrogen functionalities show excellent electrochemical performances and are explored extensively in energy storage and conversion applications. Here, we report the electrochemical supercapacitance performances of the nitrogen-doped activated carbon materials with an ultrahigh surface area prepared by the potassium hydroxide (KOH) activation of the Nelumbo nucifera (Lotus) seed in an aqueous electrolyte solution (1 M sulfuric acid: H2SO4) in a three-electrode cell. The specific surface areas and pore volumes of Lotus-seed–derived carbon materials carbonized at a different temperatures, from 600 to 1000 °C, are found in the range of 1059.6 to 2489.6 m2 g−1 and 0.819 to 2.384 cm3 g−1, respectively. The carbons are amorphous materials with a partial graphitic structure with a maximum of 3.28 atom% nitrogen content and possess hierarchically micro- and mesoporous structures. The supercapacitor electrode prepared from the best sample showed excellent electrical double-layer capacitor performance, and the electrode achieved a high specific capacitance of ca. 379.2 F g−1 at 1 A g−1 current density. Additionally, the electrode shows a high rate performance, sustaining 65.9% capacitance retention at a high current density of 50 A g−1, followed by an extraordinary long cycle life without any capacitance loss after 10,000 subsequent charging/discharging cycles. The electrochemical results demonstrate that Nelumbo nucifera seed–derived hierarchically porous carbon with nitrogen functionality would have a significant probability as an electrical double-layer capacitor electrode material for the high-performance supercapacitor applications.

Keywords

• <i>Nelumbo nucifera</i> seed
• KOH activation
• hierarchically porous carbon
• nitrogen-doping
• energy storage
• supercapacitor