Effect of Long-Term Aging on Fatigue and Thermal Cracking Performance of Polyphosphoric Acid and Styrene–Butadiene–Styrene-Modified Bio-Blend Bitumen

Abstract

Polyphosphoric acid (PPA) and styrene–butadiene–styrene (SBS) were adopted to produce PPA-SBS-modified bio-blend bitumen, which achieved excellent mechanical performance. However, its long-range performance, such as the fatigue and thermal cracking behavior under long-term thermal oxidation, is not well understood. Therefore, a pressure aging vessel (PAV) system was applied to simulate the aging behavior of the bitumen under the action of thermal oxidation. Then, a linear amplitude sweep (LAS) test combined with a viscoelastic continuum damage (VECD) model was applied to investigate the fatigue properties of the bitumen. Moreover, a bending beam rheometer (BBR) test was conducted to evaluate the thermal cracking resistance of the bitumen before and after PAV aging. Meanwhile, an atomic force microscope (AFM) was applied to observe the microscopic topography. The results show that the original compound-modified bitumen can bear more fatigue damage than that of the control bitumen at the failure point, and it also has excellent fatigue resistance at 2.5%, 5%, 7.5%, and 10% applied strain. Moreover, the VECD model can accurately predict the fatigue life of the bitumen under different applied strains. The variation ratio of stiffness modulus for the compound-modified bitumen is below that of the control bitumen after PAV aging, so it shows a better anti-aging performance. Finally, the AFM test shows that PPA and bio-bitumen decrease the heterogeneity of the bitumen, reducing the difference between phases.

Keywords

• bio-blend bitumen
• VECD model
• fatigue properties
• thermal cracking performance
• microtopography