Shellac resin effect on the properties of zein film

Abstract

In this paper, zein-based films with the addition of shellac were synthesized by lamination on the existing dry zein film (L samples) and by adding shellac alcohol solution during the synthesis of zein film in a ratio of 50-50 by casting process (M samples). Zein films without the addition of shellac were designated as control samples. Physico-chemical (thickness, moisture content and solubility), mechanical (tensile strength and elongation at break) and barrier characteristics (water vapor permeability) were examined for all samples. The resulting films were transparent, glossy, light yellow (control) to ocher (samples with shellac), flexible, and non-sticky. The results showed significantly higher values of elongation at the break of the samples with shellac (11.49% for M and 18.99% for L) compared to the control (7.14%). Significantly lower water vapor permeability values were found, 10.04 g/(m²ꞏh) for L, and 18.41 g/(m²ꞏ h) for M, compared to the control pure zein film (40.33 g/(m² ꞏh)).

Keywords

• shellac resin
• zein film
• properties