Boletín de la Sociedad Española de Cerámica y Vidrio (Aug 2000)
Factores que controlan las propiedades texturales de arcillas intercaladas con disoluciones de circonio y aluminio
Abstract
The texture development of a saponite and a montmorillonite, intercalated with zirconium and aluminium oligomers, after calcination at 500 ºC has been studied. Remarkable differences were observed among samples, depending on the source of the intercalating polycations and the parent material. On calcining, the alumina pillared clays suffered noticeable specific surface area and micropore volume losses, which have been related to the interlayer and interpillar distances of the samples. On the contrary, the zirconia pillared clays showed a slight surface area increase, which affected both micropores and mesopores and could be due to the combined effect of the thermal decomposition of the zirconium oligomers and the possible presence of mesoporous ZrO2 particles.<br><br>En este trabajo se ha estudiado la evolución de las propiedades texturales de una saponita y una montmorillonita intercaladas con disoluciones de circonio y aluminio tras calcinación a 500 ºC. Los sólidos presentaron un diferente comportamiento en función de la naturaleza de la disolución de intercalación y de la arcilla empleada. Tras calcinación, la superficie específica y el volumen microporoso de las arcillas intercaladas con disoluciones de aluminio disminuyeron de manera importante, lo cual se ha relacionado con las distancias interlaminar e interpilar que presentaron los materiales intercalados. Por contra, las superficies específicas de las arcillas intercaladas con disoluciones de circonio aumentaron, probablemente gracias al efecto combinado de la descomposición térmica de los ligandos orgánicos unidos al circonio en los policationes y la posible presencia de partículas mesoporosas de ZrO2 sobre la superficie de los sólidos.