Boletín de la Sociedad Española de Cerámica y Vidrio (Apr 2001)
Preparación y propiedades eléctricas de conductores mixtos de litio basados en oxi-sistemas vítreos
Abstract
A system based on the xLi2O-(1-x)[30V2O5-70TeO2] glassy system have been prepared by classical melt-quenching technique and their thermal and electrical properties were studied in the range from x = 0 up to 0.4. It has been observed on these glasses that with increase of Li2O concentration Tg decreases as well conductivity, however when x reaches 0.2-0.3 values conductivity begin to increase (Tg behavior remains unaltered). Results have been discussed on the basis of network modification that would occur in the glass base structure by the addition of Li2O. Those glasses show high promise as potential mixedionic materials.<br><br>El sistema vítreo xLi2O-(1-x)[30V2O5-70TeO2] ha sido preparado por la técnica tradicional de enfriamiento rápido (“melt quench”) y sus propiedades térmicas y eléctricas han sido estudiadas en el rango de x = 0 a 0.4. En este sistema se ha observado que la transición vítrea y la conductividad disminuyen a medida que aumenta la concentración de Li2O pero, por otro lado, cuando x = 0.2-0.3 la conductividad comienza a aumentar (la transición vítrea continua disminuyendo). Los resultados obtenidos se han discutido en términos de modificación de la estructura vítrea base en relación a la adición de Li2O y en términos de basicidad óptica. Estos vidrios muestras propiedades prometedores como materiales de conductividad mixta.