Effect of Aging Temperature on Microstructure, Mechanical, and Wear Properties of 18Ni-300 Maraging Steel Produced by Powder Bed Fusion

Abstract

Additive manufacturing technologies for metallic materials based on powder bed fusion have enormous industrial potential. In this study, we manufactured 18Ni-300 maraging steel using the powder bed fusion (PBF) process and investigated the effects of annealing temperatures of 430 °C, 490 °C, and 550 °C for 3 h on its microstructure, tensile fracture mechanism, and wear properties compared with the as-built specimen. The results show that annealing heat treatment effectively improved the dry sliding friction, wear properties, and room temperature tensile properties compared to the as-built specimen. Compared to other aging-treated samples, specimens that underwent heat treatment in optimal settings had superior properties. With optimal heat treatment, while melt pool boundaries remained, the cellular and columnar structures became finer compared to the un-treated specimens, and the number of dimples decreased. Consequently, the hardness and tensile strength improved by approximately 56.17% and 40.63%, respectively. The 18Ni-300 maraging steel sample that underwent heat treatment at optimal settings exhibited a coefficient of friction approximately 33.33% lower than the as-built alloy.

Keywords

• 18Ni-300 maraging steel
• powder bed fusion
• aging treatment
• microstructure
• wear behavior
• tensile test