Magnetism and Thermal Transport of Exchange-Spring-Coupled La_2/3Sr_1/3MnO₃/La₂MnCoO₆ Superlattices with Perpendicular Magnetic Anisotropy

Abstract

Superlattices (SLs) comprising layers of a soft ferromagnetic metal La2/3Sr1/3MnO3 (LSMO) with in-plane (IP) magnetic easy axis and a hard ferromagnetic insulator La2MnCoO6 (LMCO, out-of-plane anisotropy) were grown on SrTiO3 (100)(STO) substrates by a metalorganic aerosol deposition technique. Exchange spring magnetic (ESM) behavior between LSMO and LMCO, manifested by a spin reorientation transition of the LSMO layers towards perpendicular magnetic anisotropy below TSR = 260 K, was observed. Further, 3ω measurements of the [(LMCO)9/(LSMO)9]11/STO(100) superlattices revealed extremely low values of the cross-plane thermal conductivity κ(300 K) = 0.32 Wm−1K−1. Additionally, the thermal conductivity shows a peculiar dependence on the applied IP magnetic field, either decreasing or increasing in accordance with the magnetic disorder induced by ESM. Furthermore, both positive and negative magnetoresistance were observed in the SL in the respective temperature regions due to the formation of 90°-Néel domain walls within the ESM, when applying IP magnetic fields. The results are discussed in the framework of electronic contribution to thermal conductivity originating from the LSMO layers.

Keywords

• superlattices
• high-resolution STEM
• exchange spring magnet
• perpendicular magnetic anisotropy
• magneto-thermal conductivity