Effects of B4C on the formation of LPSO phase and mechanical properties of Mg–Zn–Y–Mn alloy

Abstract

Effects of B4C on the microstructure and properties of Mg94Zn2.5Y2.5Mn1 alloy were investigated by means of optical microscope, scanning electron microscope, X-ray diffraction, transmission electron microscope, nano indentation tester and electronic universal testing machine. The results indicated that the as-cast Mg94Zn2.5Y2.5Mn1 alloy was mainly composed of α-Mg, fishbone-like W phase, and block 18 R long period stacking ordered (LPSO) phase. The addition of an appropriate amount of B4C could effectively refine grains, promote the formation of the LPSO phase and inhibit the generation of the W phase. The microstructure and mechanical properties of the alloy were both optimal at the addition of 0.5 at.% B4C. The microstructure exhibited a refined grain size from 41.2 μm to 20.7 μm, and the volume fraction of the LPSO phase increased from 8.1 % to 22.5 %. The yield strength increases from 112 MPa to 145 MPa, the tensile strength of the alloy was enhanced from 192 MPa to 256 MPa, and the elongation increased from 4.8 % to 8.6 %.

Keywords

• Magnesium alloy
• Long period stacking ordered structure
• Microstructure
• Mechanical property