Comparative Studies on Two Types of OSB Boards Obtained from Mixed Resinous and Fast-growing Hard Wood

Abstract

The paper aims to compare the oriented strand boards (OSBs) made in the laboratory from a mixture of softwood species to those made from hardwood species, followed by their comparison to European and industry standards. In this regard, the main properties of the panels made in the laboratory were determined, including density, absorption, and swelling in thickness, modulus of elasticity, modulus of rupture, and internal bond. The analysis of the properties of swelling (24 h) and absorption (24 h) revealed that the mixture of softwood species was slightly better thanthe hardwood one. It was also shown that the panels manufactured from the mixture of hardwood species had better mechanical properties than those made of the softwood mixture (modulus of rupture (MOR) = 43.48 N/mm2, modulus of elasticity (MOE) = 7253 N/mm, and internal bond (IB) = 1.57 N/mm2). Additionally, the comparative analysis of properties indicates that the density is highly significant in determining the MOE values of the OSBs. This will allow softwood speciestobe replaced with other species of soft and fast-growing deciduous trees such as willow, birch, and poplar in the manufacture of oriented strand boards.

Keywords

• oriented strand boards (OSBs)
• fast-growing species, modulus of rupture (MOR)
• modulus of elasticity (MOE)
• internal bond (IB)
• swelling (S)
• water absorption (A)