Applied Sciences (Oct 2020)

The Effect of Addition of Antioxidant 1,2-dihydro-2,2,4-trimethyl-quinoline on Characteristics of Crepe Rubber Modified Asphalt in Short Term Aging and Long Term Aging Conditions

  • Bahruddin Ibrahim,
  • Arya Wiranata,
  • Alfian Malik

DOI
https://doi.org/10.3390/app10207236
Journal volume & issue
Vol. 10, no. 20
p. 7236

Abstract

Read online

The use of natural rubber to resist bitumen is usually prone to degradation and aging. One method to overcome this problem is the addition of antioxidants. This study aims to determine the effect of the addition of antioxidants 1,2-dihydro-2,2,4-trimethyl-quinoline (TMQ) on natural rubber modified asphalt crepe rubber and its performance in short-term and long-term aging conditions. The modified rubber asphalt mixture’s manufacture begins by melting the crepe rubber at 200 °C before being mixed in asphalt at 165 °C. Addition of antioxidant TMQ during the stirring process of the mixture of asphalt and melted rubber. The crepe rubber content was 8, 10, and 12% w/w, while the TMQ content was 1, 2, and 3% w/w of the total sample weight. The modified asphalt samples’ characterization included penetration, softening point, weight loss after a rolling thin film oven test (RTFOT), penetration after RTFOT, and Marshall test. Review of the performance of asphalt under short-term aging conditions using a dynamic shear rheometer (DSR). Evaluation of asphalt performance under long-term aging conditions using Fourier-transform infrared spectroscopy (FTIR). The results showed that the fact that the best-modified asphalt product was the addition of 10% crepe rubber and 2% TMQ. The best-modified asphalt characteristics have penetration 68.70 dmm, softening point 55.45 °C, weight loss only 0.0579%, penetration after RTFOT 59.60, Marshall stability 1403.96 kg with optimum asphalt content of 5.50%, and rutting factor (G*/Sinδ) 6.91 kPa and 16.1 kPa before and after RTFOT. Overall, the modified crepe rubber asphalt can improve the performance of the asphalt in terms of durability. Simultaneously, the antioxidant TMQ works very well in increasing the resistance of bitumen to aging in the conditions of short-term aging and long-term aging.

Keywords