Extraction of Tantalum Powder via the Magnesium Reduction of Tantalum Pentoxide

Abstract

The metallic tantalum powder was successfully synthesized via reduction of tantalum pentoxide (Ta2O5) with magnesium gas at 1073~1223 K for 10 h inside the chamber held under an argon atmosphere. The powder obtained after reduction shows the Ta⁻MgO mixed structure and that the MgO component was dissolved and removed fully via stirring in a water-based HCl solution. The particle size in the tantalum powder obtained after acid leaching was shown to be in a range of 50~300 nm, and the mean internal crystallite sizes measured by the Scherrer equation varied from 11.5 to 24.7 nm according to the increase in reduction temperatures. The temperature satisfactory for a maximal reduction effect was found to be 1173 K because the oxygen content was minimally saturated to about 1.3 wt %.

Keywords

• tantalum powder
• magnesium reduction
• Ta₂O₅ powder
• MgO
• HCl solution