Multiferroic and ferroelectric phases revealed in 2D Ti3C2Tx MXene film for high performance resistive data storage devices

Abstract

Abstract Multiferroic materials, showing simultaneous ferroelectric and ferromagnetic orders, are considered to be promising candidates for future data storage technology however, the multiferroic phenomenon in two-dimensional (2D) materials is rarely observed. We report a simple approach to observe frequency-dependent ferroelectricity and multiferroicity in 2D Ti3C2T x MXene film at room-temperature. To study the frequency and poling effect on ferroelectricity, we performed electric polarization vs. electric field (P-E) measurement at different frequencies, measured under zero and non-zero static magnetic fields. The results not only indicate a clear frequency dependence of electric domains owing to varying time relaxation during reversal dynamic but also showed magnetic field control of electric polarization thus, confirmed the presence of strong magneto-electric (ME) coupling at room-temperature. The existence of ME coupling was attributed to the coupling between disordered electric dipoles with local spin moments as well reduced dielectric loss after heat-treatment. Moreover, the ferroelectric Ti3C2T x MXene film was employed as an active layer within the resistive data storage device that showed a stable switching behavior along with improved on/off ratio in comparison to non-ferroelectric Ti3C2T x active layer. The unique multiferroic behavior along with ferroelectric-tuned data storage devices reported here, will help understand the intrinsic nature of 2D materials and will advance the 2D ferroelectric data storage industry.