Electrochemical Studies of Pd-Based Anode Catalysts in Alkaline Medium for Direct Glycerol Fuel Cells

Abstract

This study investigates the most effective electrocatalyst for glycerol oxidation reaction (GOR) in alkaline medium for five synthesized electrocatalysts, Pd, PdNi, PdNiO, PdMn3O4 and PdMn3O4NiO, supported on multi-walled carbon nanotubes (MWCNTs) prepared using the polyol method. The particle size and crystalline size of the electrocatalysts were determined using HR-TEM and XRD techniques, respectively, while EDS was used to determine the elemental composition. XRD showed crystalline sizes ranging from 3.4 to 10.1 nm, while HR-TEM revealed particle sizes within the range of 3.4 and 7.2 nm. The electroactivity, electron kinetics and stability of the electrocatalysts towards glycerol in alkaline medium was evaluated using linear sweep voltammetry (LSV), electrochemical impedance spectroscopy (EIS) and chronoamperometry (CA), respectively, while the electroactive surface area (ECSA) of the electrocatalysts was determined using cyclic voltammetry (CV). The metal oxide-based Pd electrocatalysts PdNiO and PdMn3O4 were the most electrochemically active, while the addition of the second metal oxide to the Pd electrocatalyst PdMn3O4NiO did not show any improvement. This was associated with this electrocatalyst having the highest particle and crystalline sizes.

Keywords

• glycerol oxidation
• electrocatalysts
• multi-walled carbon nanotubes
• metal oxides