Obtaining Foamed Glass-Ceramics from Diamond Concentration Tailings

Abstract

The possibility of obtaining building foamed glass-ceramic using the diamond concentration tailings of the Lomonosov deposit in Arkhangelsk Region, Russia, is demonstrated here. The effect of the tailings’ particle size distribution, feed temperature, the addition of a foaming agent, and the content of oxidizer on the feed charge foaming is established. The process conditions for obtaining foamed glass-ceramic materials are described. The specifications of the materials with the optimal composition (tailings 50 wt.%, glass waste 50 wt.%, SiC 0.5 wt.%, Fe2O3 1 wt.%) foamed at 1020–1050 °C were as follows: apparent density 0.23–0.51 g/cm3, compression strength 0.58–2.40 MPa, water absorption (by volume) 8.7–19.0%. Based on the combination of the measured properties when used in dry conditions, the obtained materials can be considered heat-insulating foam materials. The thermal conductivity was 0.060–0.066 W/m·K.

Keywords

• foamed glass-ceramics
• diamond concentration tailings
• waste glass
• apparent density
• compressive strength
• water absorption