Stress Rupture and Precipitation Behavior of TP310HCbN(HR3C) for Supercritical Boilers

Abstract

Using persistent experiment method, combined with Gleeble,hardness analysis, SEM, EDS, TEM and other analytical methods, the hot deformation, stress rupture and precipitation behavior of TP310HCbN heat resistance steel was analysed at 650℃ and 700℃, the results show that:the change of the hardness is not obviously under two different stress rupture temperature; with stress rupture time prolongs, TP310HCbN heat-resistant steel intragranular precipitates from granular into rod-shaped, and presence of wormlike NbCrN rich precipitates and dislocation interactions; Taiyuan Iron and Steel production of TP310HCbN heat-resistant steel at 650/700℃-100000h extrapolation lasting strength meet the standard requirements.

Keywords

• TP310HCbN
• precipitation phase
• stress rupture
• hardness