Investigation of anticorrosive behaviour of novel tert-butyl 4-[(4-methyl phenyl) carbonyl] piperazine-1-carboxylate for carbon steel in 1M HCl

Abstract

The main focus of current research is on the synthesis and anticorrosive activity of novel heterocyclic compounds tert-butyl 4-[(4-methyl phenyl) carbonyl] piperazine-1-carboxylate [TBMPCPC]. Electrochemical, quantum chemical, and surface characterization studies at elevated temperatures (303–333 K) for carbon steel in 1M HCl solution studied this molecule's corrosion inhibition property. It is observed from the results of electrochemical studies that the TBMPCPC may be able to effectively protect the steel plate surface with an inhibition efficiency of 91.5 % at 25 ppm in corrosive media. The corrosion inhibition depends on concentration, as concentration also increases inhibition efficiency due to the strong and spontaneous adsorption on the metal's surface. The Tafel polarization measurements concluded that the inhibitor works as a mixed form to protect the carbon steel in the bulk solution from corrosion. The adsorption of the TBMPCPC onto the metal surface was in reliable with the isothermal model of the Langmuir adsorption. The scanning electron microscopy clearly showed that the inhibitor was substantially deposited on the metal surface, indicating substantial inhibition. The surface morphology of carbon steel in the absence and existence of an inhibitor in 1 M HCl is also studied using the Atomic Force Microscopic method.

Keywords

• TBMPCPC
• Corrosion inhibition
• Electrochemical
• SE