Difference of Microstructures and Mechanical Properties between 9Cr-1W Ferritic/martensitic Steel and ODS Steel

Abstract

Ferrtic/martensitic and ODS steels were fabricated by the mechanical alloying process, and their microstructures and mechanical properties were investigated. The 9Cr-1W and 9Cr-1W-0.3Ti-0.35Y2O3 (in wt.%) steels were prepared by the same fabrication process such as mechanical alloying, hot isostatic pressing, and hot rolling processes. A microstructural observation of these steels indicated that the Ti and Y2O3 additions to 9Cr-1W steel were significantly effective to refine the grain size and form nano-sized Y-Ti-O oxide particles. As a result, the tensile strengths at room and elevated temperatures were considerably enhanced. Considerable improvement of the creep resistances at 700°C was also evaluated. It is thus concluded that 9Cr-1W ODS steel with Ti and Y2O3 additions would be very effective in improving the mechanical properties especially at elevated temperatures.

Keywords

• 9cr-1w steel
• oxide dispersion strengthening (ods)
• grain refinement
• nano-oxide particle
• creep resistance