Investigations of LiNb_1−<i>x</i>Ta<i>_x</i>O₃ Nanopowders Obtained with Mechanochemical Method

Abstract

Nanocrystalline compounds LiNb1−xTaxO3 of various compositions (x = 0, 0.25, 0.5, 0.75, 1) were synthesized by high-energy ball milling of the initial materials (Li2CO3, Nb2O5, Ta2O5) and subsequent high-temperature annealing of the resulting powders. Data on the phase composition of the nanopowders were obtained by X-ray diffraction methods, and the dependence of the structural parameters of LiNb1−xTaxO3 compounds on the value of x was established. As a result of the experiments, the optimal parameters of the milling and annealing runs were determined, which made it possible to obtain single-phase compounds. The Raman scattering spectra of LiNb1−xTaxO3 compounds (x = 0, 0.25, 0.5, 0.75, 1) have been investigated. Preliminary experiments have been carried out to study the temperature dependences of their electrical conductivity.

Keywords

• nanoparticles
• nanopowders
• lithium niobate-tantalate
• X-ray diffraction
• Raman spectroscopy
• temperature dependence of electroconductivity