Effect of Silane Coupling Agents on the Rheology, Dynamic and Mechanical Properties of Ethylene Propylene Diene Rubber/Calcium Carbonate Composites

Abstract

The effects of three trimethoxysilanes with different functional groups on the rheology, dynamic and mechanical properties of ethylene propylene diene rubber (EPDM)/calcium carbonate (CaCO3) composites were investigated respectively. The results showed that the addition of silane increased the value of MH and MH–ML of the compounds. Geniosil XL 33 silane decreased the shear modulus of the EPDM/CaCO3 compounds, and the bound rubber content increased slightly with the addition of vinyl trimethoxy silane (VTMS) and methylacryloxy-methyltrimethoxysilane (Geniosil XL 33) silane in the compounds. The vulcanizates with the addition of the VTMS and Geniosil XL 33 silane showed a significant increase in tensile strength and abrasion resistance; however, ethyltrimethoxysilane (ETMS) silane weakened the tensile strength and abrasion resistance of the vulcanizates. At low strain, the cross-linking and reaggregation of fillers resulted in a high storage modulus of vulcanizates with silane. When the strain exceeded 10%, the storage modulus of the vulcanizates with the Geniosil XL 33 and VTMS silane was higher. The loss modulus and tan δ of the vulcanized rubber with the Geniosil XL 33 and VTMS silanes were lower compared to the ETMS and 0 silane.

Keywords

• silane
• interaction
• cross-link