Due to their excellent properties, antimicrobial fiber membranes are widely applied in bioprotective materials. This work addresses the preparation of thermoplastic polyurethane (TPU)-based fiber membranes with active antimicrobial properties. 2-hydroxypropyl trimethyl ammonium chloride-terminated hyperbranched polymer (HBP-HTC) was synthesized and used as an antimicrobial agent. The fiber membranes were obtained by electrospinning a mixed solution of HBP-HTC and TPU. Different electrospinning conditions were investigated, such as the spinning voltage and drum rotation speed. The fiber membrane prepared under a 22 kV anode voltage and 100 rpm rotation speed had an average fiber diameter of 1.66 μm with a concentrated diameter distribution. Antibacterial tests showed that when the fiber membrane was loaded with 1500 mg/kg of HBP-HTC, the antibacterial rates of E. coli as well as S. aureus both reached 99.99%, exhibiting excellent proactive antimicrobial performance. Moreover, the protective performance of the fiber membrane was outstanding, with a filtration efficiency of 99.9%, a hydrostatic pressure resistance greater than 16,758 Pa, and a moisture permeability of 2711.0 g⋅(m2⋅d)−1.