Journal of the Serbian Chemical Society (Dec 2009)

Mechanochemical synthesis and electrical conductivity of nanocrystalline delta-Bi2O3 stabilized by HfO2 and ZrO2

  • LJILJANA KARANOVIĆ,
  • DEJAN POLETI,
  • ČEDOMIR JOVALEKIĆ,
  • MIODRAG ZDUJIĆ

Journal volume & issue
Vol. 74, no. 12
pp. 1401 – 1411

Abstract

Read online

A powder mixture of a-Bi2O3 and HfO2, in the molar ratio 2:3, was mechanochemically treated in a planetary ball mill under air, using zirconium oxide vials and balls as the milling medium. After 50 h of milling, the mechanochemical reaction led to the formation of a nanocrystalline a-Bi2O3 phase (fluorite-type solid solution Bi0.87Hf0.59Zr0.63O3.61), with a crystallite size of 20 nm. The mechanochemical reaction started at a very beginning of milling accompanied by an accumulation of ZrO2 arising from the milling tools. The samples prepared after various milling times were characterized by X-ray powder diffraction and DSC analysis. The electrical properties of the as-milled and pressed Bi0.87Hf0.59Zr0.63O3.61powder were studied using impedance spectroscopy in the temperature range from 100 to 700 °C under air. The electrical conductivity was determined to be 9.43×10-6 and 0.080 S cm-1 for the temperatures of 300 and 700 °C, respectively.

Keywords