Sustainable composite materials based on ethylene-vinylacetate copolymer and organo-modified silica

Abstract

Silica nanoparticles (SNPs) were modified by different amounts of 3-aminopropyltriethoxysilane (APTES). Nanocomposites based on ethylene vinyl acetate copolymer (EVA) and modified SNP (m-SNP) were prepared by the melt mixing method. They were characterized by Haake torque measurement, differential scanning calorimetry (DSC), horizontal burning test, scanning electron microscopy. Accelerated weather testing of the nanocomposites was performed according to ASTM D4329 (cycle A) for 168 h. The Haake torque indicates that the relative melt viscosity of EVA/m-SNPs is slightly higher than that of EVA/SNP nanocomposites. The DSC and burning test results show that m-SNPs decrease crystallinity degree and flammability of EVA. After accelerated weather testing, the relative amount of C=O groups in EVA/m-SNP nanocomposites is lower than that in EVA/SNP nanocomposites. Micro crack of EVA/m-SNP nanocomposite is smaller than that of EVA/SNP nanocomposite. In our study, the EVA/m-SNP nanocomposites with good tensile properties, flame and weather resistance can be used as sustainable materials in some technique fields.

Keywords

• accelerated weathering resistance
• aptes
• ethylene-vinyl acetate copolymer
• eva
• silica nanoparticles