Anti-corrosion performance of ethyl dimethyl propylammonium bis (trifluoromethyl sulfonyl) imide (EDMPA-TFSI) for AA3003 alloy in acid chloride solutions in the presence and absence of potassium iodide

Abstract

This work aims to evaluate the anti-corrosion potential of ethyl dimethyl propylammonium bis (trifluoromethyl sulfonyl) imide (EDMPA-TFSI)-ionic liquid on AA3003 alloy in 0.5 M HCl solution in the presence and absence of potassium iodide at ambient and elevated temperatures. The corrosion inhibition of AA3003 alloy by EDMPA-TFSI in the presence of potassium iodide was evaluated using hydrogen evolution measurements at 303 K and 333 K. The results show that in the absence of potassium iodide, EDMPA-TFSI decelerates AA3003 corrosion in an acidic medium with a maximum inhibition efficiency of 93.2 % and 90.5 % obtained at 303 K and 333 K respectively. In the presence of potassium iodide, 94.7 % and 89.8 % inhibition efficiencies were obtained at 303 K and 333 K, respectively. This adsorption behavior is concordant with the Langmuir adsorption isotherm and the corrosion process in the presence of EDMPA-TFSI shows consistency with first-order reaction kinetics. New information on the application of EDMPA-TFSI as a workable corrosion inhibitor is provided herein.

Keywords

• Ionic liquids
• Aluminum
• Corrosion
• Inhibition
• Acid