PERFORMANCE OF AN ENVIRONMENTAL PROTECTION LINER AFTER LABORATORY UV EXPOSURE

Abstract

High-density polyethylene (HDPE) geomembranes are commonly used as an environmental protection liner due to their good chemical and mechanical resistances and low cost. Ultraviolet (UV) radiation is an essential issue in durability studies for pond applications. This study evaluated a 1.5-mm thick HDPE geomembrane exposed to ultraviolet fluorescent radiation for 8760 h in a laboratory and thermoanalytical and physical analyses were conducted towards the understanding of its performance after exposure. According to the results, although the geomembrane maintained the ductile behavior, it showed a 52.48% final decrease in stress crack resistance (SCR) compared to virgin SCR. Moreover, a considerable antioxidant depletion occurred after 8760 h exposure shown by the Std. OIT (standard oxidative-induction time) results, demonstrating a Std. OIT value decrease of 89.19% compared to the virgin Std. OIT. Such a behavior contributed to the susceptibility of thermal effects in the DSC (differential scanning calorimetry) curves and the losses observed in the SCR values, attesting the geomembrane’s oxidative degradation mechanism occurred and changed the polymer’s structure.

Keywords

• geomembrane
• high-density polyethylene
• ultraviolet radiation
• durability
• physical and thermal analysis