Bioactivity, Cytotoxicity, and Tribological Studies of Nickel-Free Austenitic Stainless Steel Obtained via Powder Metallurgy Route

Abstract

In the present study, the bioactivity, cytotoxicity, and tribological properties of a nickel-free austenitic stainless steel produced via the mechanical alloying of elemental iron, chromium, and manganese nitride powders following by hot isostatic pressing was investigated. Powders after 90 h of mechanical alloying were consolidated via hot isostatic pressing at 1150 °C (1425 K) and heat treated at 1175 °C (1448 K) for 1 h in a vacuum with furnace cooling. Tribological tests were performed to determine the resistance of the as-received nickel-free steel. It was noticed that applying heat treatment after hot isostatic pressing decreases the average friction coefficient and wear rate of the austenitic steel. An immersion test in a simulated body fluid for 28 days at 37 ± 1 °C has been used to determine the biocompatibility of the tested material. The SEM-EDS analysis allowed us to characterise the morphology of the films and the elements of the steel on the thin-film layer. Elements typical of apatite (calcium and phosphorus) were detected on the surface of the sample. Cellular toxicity tests showed no significant toxic side effects for Saos-2 human osteosarcoma cells and the number of Saos-2 human osteosarcoma cells on the nickel-free steel was greater than on the 316LV grade steel.

Keywords

• nickel-free austenitic stainless steel
• powder metallurgy
• wear resistance
• bioactivity
• cytotoxicity