Tribological Behavior of Hydrocarbons in Rolling Contact

Abstract

In the analysis of tribological contacts, the focus is often on a singular question or result. However, this entails the potential risk that the overall picture and the relationships could be oversimplified or even that wrong conclusions could be drawn. In this article, a comprehensive consideration of test results including component and lubricant analyses is demonstrated by using the example of rolling contact. For this purpose, thrust cylindrical roller bearings of type 81212 with unadditized base oils were tested in the mixed-friction area. Our study shows that by using an adapted and innovative surface analysis, a deeper dive into the tribo-film is feasible even without highly sophisticated analytical equipment. The characterization of the layers was performed by the three less time-consuming spatially resolved analysis methods of µXRF, ATR FTIR microscopy and Raman spectroscopy adapted by Schaeffler. This represents a bridge between industry and research. The investigations show that especially undocumented and uncontrolled contamination of the test equipment could lead to surprising findings, which would result in the wrong conclusions. Simple substances, like hydrocarbons, are demanding test specimens.

Keywords

• rolling bearing
• tribology
• polyalphaolefin
• lubrication