In situ TEM study of precipitation in a quasicrystal-strengthened AL-alloy

Abstract

Precipitation kinetics and mechanisms within an Al-Mn-Be-Cu quasicrystal strengthened alloy at 300°C were studied using in-situ transmission electron microscopy. The alloy was cast into a copper mould. Quasicrystalline precipitates formed throughout the Al-rich solid solution, whilst heterogeneous formations of Al2Cu and T-phase occurred on icosahedral quasicrystalline particles formed during solidification. The formation of quasicrystalline particles and T-phase was limited by manganese diffusivity, whilst that of Al2Cu by copper diffusivity. The precipitation produced only a small hardening effect.

Keywords

• precipitation
• Al-alloy
• transmission electron microscopy (TEM)
• quasicrystal