High temperature capture of CO2 on Li4SiO4 sorbents via a simple dry ball-milling coupled with K2CO3 physical addition

Abstract

The reversible CO2 absorption/desorption of lithium orthosilicate (Li4SiO4) sorbents holds potential for high temperature capture of CO2 from hot flue gases, sorption-enhanced reforming and solar thermochemical energy storage. In this study, we have prepared a series of Li4SiO4 sorbents using a combination of K2CO3 addition and dry ball-milling procedure to improve the relatively slow kinetics under low CO2 partial pressure conditions. The synergistic effects of dry ball-milling and K2CO3 addition on the intrinsic properties of Li4SiO4 sorbents were explored by thermogravimetric analysis and structural characterizations. Thermogravimetric analysis indicate that the highest CO2 uptakes were achieved with dry ball-milling combined with K2CO3 physical addition. The structural characterizations further reveal that this sorbent (P-3K-1.5 M) had the smallest crystallite/particle size, largest surface area, and highest availability of surface alkaline-sites. The kinetics analysis also demonstrates that P-3K-1.5 M exhibited the fastest sorption kinetics during a double process. Additionally, P-3K-1.5 M maintained a high capacity over 10 sorption/desorption cycles. Therefore, this synthesis technique, which is simple, cost-effective, and easily scalable, shows great promise for high-temperature CO2 capture.

Keywords

• CO2 capture
• K2CO3 doping
• Milling
• Li4SiO4