New avenues for residual stress analysis in ultrathin atomic layer deposited free-standing membranes through release of micro-cantilevers

Abstract

The fabrication of thinnest, yet undeformed membrane structures with nanometer resolution is a prerequisite for a variety of Microelectromechanical systems (MEMS). However, functionally relevant thin films are susceptible to growth-generated stress. To tune the performance and reach large aspect ratios, knowledge of the intrinsic material properties is indispensable. Here, we present a new method for stress evaluation through releasing defined micro-cantilever segments by focused ion beam (FIB) milling from a predefined free-standing membrane structure. Thereby, the cantilever segment is allowed to equilibrate to a stress-released state through measurable strain in the form of a resulting radius of curvature. This radius can be back-calculated to the residual stress state. The method was tested on a 20 nm and 50 nm thick tunnel-like ALD Image 1 membrane structure, revealing a significant amount of residual stress with 866 MPa and 6104 MPa, respectively. Complementary finite element analysis to estimate the stress distribution in the structure showed a 97% and 90% agreement in out-of-plane deflection for the 20 nm and 50 nm membranes, respectively. This work reveals the possibilities of releasing entire membrane segments from thin film membranes with a significant amount of residual stress and to use the resulting bending behavior for evaluating stress and strain by measuring their deformation.

Keywords

• Ultrathin membranes
• FIB
• Residual stress
• Strain analysis
• ALD