Magnesium Oxide and Magnesium Fluoride Nanopowders Produced in a Diffuse Nanosecond Discharge in Argon

Abstract

The synthesis of the nanopowders of magnesium oxide and magnesium fluoride during the operation of a repetitive diffuse nanosecond discharge in argon at various pressures was performed. Nanosecond voltage pulses with an amplitude of −70 kV, a rise time of 0.7 ns, and a duration of 0.7 ns were applied across a point-to-plane gap of 2 mm in length. The pulse repetition rate was 60 Hz. The high-voltage pointed electrode was made of magnesium. A diffuse discharge cold plasma was formed under these conditions. Nanoparticles were produced as a result of an explosion of microprotrusions on the surface of the magnesium electrode duo to a high current density. Lines of magnesium atoms and ions were observed in the emission optical spectrum. Under the actions of the gas dynamics processes caused by the plasma channel expansion during the interpulse period, nanoparticles were deposited onto the surface of the grounded plane electrode and the side wall of the gas discharge chamber. The morphology, elemental, and phase composition of the powders were studied using transmission electron microscopy (TEM) and energy-dispersive X-ray spectroscopy (EDS).

Keywords

• magnesium
• magnesium oxide
• magnesium fluoride
• nanopowder
• ceramics
• diffuse nanosecond discharge