Lubricants (May 2022)

Investigation of the Wettability Properties of Different Textured Lead/Lead-Free Bronze Coatings

  • Amani Khaskhoussi,
  • Giacomo Risitano,
  • Luigi Calabrese,
  • Danilo D’Andrea

DOI
https://doi.org/10.3390/lubricants10050082
Journal volume & issue
Vol. 10, no. 5
p. 82

Abstract

Read online

Hydraulic components are often subjected to sliding contacts under starved or mixed lubrication. The condition of starved lubrication occurs during the start-up phase of the hydraulic machines or at low working temperature, causing friction and wear of components such as the cylinder block or the valve plate. The aim of this paper was to evaluate the hydrophobicity and oleophilic behavior of lead/lead-free bronze coatings under different texture conditions obtained by varying the diameter and the density of the dimples. The wettability tests were performed using sessile drop tests with oil and water liquids. The dimple parameters were analyzed using confocal microscopy, while the XRF analyses were performed to evaluate the composition of the bronze coatings. Based on the wettability measurements using oil and water, it was possible to assess that the porous surface acted as oil reservoirs that could prolong the life of lubricating oil layer, and may have resulted in a superior wear resistance. Furthermore, a relevant hydrophobicity was highlighted, suggesting that the surface texturing promoted the water-repellent barrier action on the surface. The experimental results showed that the discrepancy in surface properties in oil and water was raised when using the lead bronze coating. These coupled oleophilic and hydrophobic behaviors could play a beneficial role in sustaining the durability of a lubricating oil layer under a condition of continuous water-droplet impact.

Keywords