ESBR Nanocomposites Filled with Monodisperse Silica Modified with Si747: The Effects of Amount and pH on Performance
Lijian Xia,
Anmin Tao,
Jinyun Cui,
Abin Sun,
Ze Kan,
Shaofeng Liu
Affiliations
Lijian Xia
Key Laboratory of Biobased Polymer Materials, Shandong Provincial Education Department, School of Polymer Science and Engineering, Qingdao University of Science and Technology, Qingdao 266042, China
Anmin Tao
Key Laboratory of Biobased Polymer Materials, Shandong Provincial Education Department, School of Polymer Science and Engineering, Qingdao University of Science and Technology, Qingdao 266042, China
Jinyun Cui
Key Laboratory of Biobased Polymer Materials, Shandong Provincial Education Department, School of Polymer Science and Engineering, Qingdao University of Science and Technology, Qingdao 266042, China
Abin Sun
Key Laboratory of Biobased Polymer Materials, Shandong Provincial Education Department, School of Polymer Science and Engineering, Qingdao University of Science and Technology, Qingdao 266042, China
Ze Kan
Key Laboratory of Biobased Polymer Materials, Shandong Provincial Education Department, School of Polymer Science and Engineering, Qingdao University of Science and Technology, Qingdao 266042, China
Shaofeng Liu
Key Laboratory of Biobased Polymer Materials, Shandong Provincial Education Department, School of Polymer Science and Engineering, Qingdao University of Science and Technology, Qingdao 266042, China
To prepare silica/rubber composites for low roll resistance tires, a novel strategy was proposed in this study, in which autonomous monodisperse silica (AS) was prepared and modified using 3-mercaptopropyloxy-methoxyl-bis(nonane-pentaethoxy) siloxane (Si747), after which silica/emulsion styrene butadiene rubber (ESBR) master batches were produced using the latex compounding technique. Meanwhile, the commercial precipitated silica (PS) was introduced as a control. In this study, the effects of amount of Si747 and pH value on the properties of the silica/ESBR composites were systematically analyzed. Thermal gravimetric analysis (TGA) and Fourier transform infrared (FTIR) results indicated that Si747 reduced the silanol group by chemical grafting and physical shielding, and the optimum amounts of Si747 for AS and PS modification were confirmed to be 15% and 20%, respectively. Under a pH of 9, ESBR/modified AS (MAS) composites with 15% Si747 presented better silica dispersion and a weaker Payne effect, compared with ESBR/modified PS (MPS) composites with 20% Si747. Meanwhile, in terms of dynamic properties, the ESBR/MAS composites exhibited a better balance of lower rolling resistance and higher wet skid resistance than the ESBR/MPS composites.