Transformation of Coherent Twin Boundary into Basal-Prismatic Boundary in HCP-Ti: A Molecular Dynamics Study

Abstract

The manufacturing process for wrought Ti alloys with the hexagonal close-packed (HCP) structure introduces a complicated microstructure with abundant intra- and inter-grain boundaries, which greatly influence performance. In the hexagonal close-packed (HCP) structure, two types of grain boundaries are commonly observed between grains with ~90° misorientation: the basal/prismatic boundary (BPB) and the coherent twin boundary (CTB). The mechanical response of the BPB and CTB under external loading was studied through molecular dynamic simulations of HCP-Ti. The results revealed that CTB undergoes transformation into BPB through the accumulation of twin boundary (TB) steps and subsequent emission of Shockley partial dislocations. When the total mismatch vector is close to the Burgers vector of a Shockley partial dislocation, BPB emits partial dislocations and further grows along the stacking faults. When a pair of CTBs are close to each other, severe boundary distortion occurs, facilitating the emission and absorption of partial dislocations, which further assists the CTB-BPB transformation. The present results thus help to explain the frequent observation of coexisting CTB and BPB in HCP alloys and further contribute to the understanding of their microstructure and property regulation.

Keywords

• titanium
• grain boundary
• dislocation
• plastic deformation
• molecular dynamics