Influence of whitening additives on the properties of decorative slag-alkali cements and mortars

Abstract

The paper shows a comparative study of the influence of whitening additives (kaolin, TiO2 and СаСО3) on the production of decorative alkali-activated slag cement and mortars with a degree of whiteness of at least 70%; as well as their influence on the structure formation and evolution of physico-mechanical properties. According to results obtained, kaolin provides chemical bonding of Na+ into insoluble zeolite-like compounds; and CaCO3 densifies the structure and reduces shrinkage deformations. At the early stages of hardening (up to 7 days), the additions of kaolin and calcite, due to their significant amount (15 and 24%), reduces the compressive strength of the cement paste; nevertheless, at later ages (until 90 days) the difference in strength almost disappears. The high colourfastness and weather resistance of pigmented cements under the influence of ultraviolet radiation and freeze/thaw cycles has been established. A comparative assessment of the economic efficiency has shown that СаСО3 is the best cost-effective additive.

Keywords

• Alkali-activated slag cements
• Colour stability
• Pigments
• Decorative cements
• Freeze/thaw resistance
• Behaviour