Preparation of Low-Molecular-Weight Polyacrylamide as the Delayed Crosslinking Plugging Agent for Drilling Fluid

Abstract

Deep wells and ultra-deep wells often encounter cracks, karst caves, and other developed strata, which can lead to leakage during drilling. Conventional bridge slurry plugging technology is prone to leaking due to the poor plugging effect of the plugging agent. The gel plugging agent possesses characteristics of flexible plugging and adaptive matching of formation leakage channels. It can fill cracks or caves and enhance the pressure-bearing capacity of the formation. A controllable crosslinking plugging agent based on low-molecular-weight polyacrylamide was studied. Polyacrylamide with different molecular weights is synthesized from acrylamide and an initiator. A crosslinking time-controllable polymer is synthesized from low-molecular-weight polyacrylamide by adding crosslinking agent and retarder. The low-molecular-weight polyacrylamide plugging agent has low viscosity before gelation and good fluidity in the wellbore. After being configured on the ground, it is transported by pipeline and sent underground to reach the thickening condition. The gel solution rapidly solidifies, and its strength improves after high-temperature crosslinking. The synthesis conditions of the polymer were as follows: a monomer concentration of 9%, initiator 3.5%, synthesis temperature of 65 °C, and hydrogen peroxide initiator. The optimal formula of the gel plugging agent is as follows: a polymer concentration of 6%, a crosslinking agent concentration of 1%, and a retarder concentration of 8%. The generated polymer molecular structure contains amide groups. This crosslinking time-controllable plugging agent based on low-molecular-weight polyacrylamide has stable rheology, and its temperature resistance can reach 150 °C. At 150 °C, the gelation time can be controlled by adjusting the concentration of retarder, and the longest can reach 4 h. The plugging efficiency of the gel plugging agent is more than 95%. With the increase in seam width, the pressure of the gel plugging agent gradually decreases.

Keywords

• delayed crosslinking
• low viscosity
• plugging material
• polymer gel
• well leakage