Analysis of Influencing Factors in the Preparation of Mullite Whiskers from Recovering Silicon-Rich Waste under Low-Temperature Conditions

Abstract

A large amount of catalyst waste containing silicon is deposited or buried every year, resulting in serious environmental pollution and a waste of resources. In this paper, a method to prepare mullite whiskers by recycling silica-rich waste under low-temperature conditions was investigated. The effects of raw materials, sintering temperature, catalyst addition, holding time and co-solvent addition on the structure, morphology and phase transition of the synthesized whiskers were investigated and characterized with SEM, XRD, TEM, TG and DTA. The results show that the addition of 10% Na2SO4 as the liquid-phase mass transfer medium could effectively improve the crystallization efficiency of mullite whiskers, while providing an ideal living environment for the growth of whiskers. The crystallinity and uniformity of mullite were positively correlated with the addition of aluminum fluoride trihydrate and the holding time, respectively. The growth law and conditions of mullite whiskers are discussed, and the optimal growth process conditions of mullite whiskers were optimized. The optimal conditions for mullite whiskers were determined as follows: the addition of aluminum fluoride is 5 wt%, the sintering temperature is 825 °C, and the holding time is 5 h at the time of sintering. This work offers new prospects for the industrial production of mullite whiskers from recycled silica-rich waste.

Keywords

• silicon-rich
• mullite whiskers
• low temperature
• sintering temperature
• keep-warm time