Effects of Hot Isostatic Pressing on the Properties of Laser-Powder Bed Fusion Fabricated Water Atomized 25Cr7Ni Stainless Steel

Abstract

25Cr7Ni stainless steel (super duplex stainless steels) exhibits a duplex microstructure of ferrite and austenite, resulting in an excellent combination of high strength and corrosion resistance. However, Laser-Powder Bed Fusion fabrication of a water-atomized 25Cr7Ni stainless steel of novel chemical composition resulted in a purely ferritic microstructure and over 5% porosity. The current study investigated the effects of two hot isostatic pressing parameters on the physical, mechanical, and corrosion properties as well as microstructures of water-atomized 25Cr7Ni stainless steel of novel composition fabricated by L-PBF for the first time in the literature. The corrosion behaviour was studied using linear sweep voltammetry in a 3.5% NaCl solution. The Hot Isostatic Pressing-treated sample achieved over 98% densification with a corresponding reduction in porosity to less than 0.1% and about 3~4% in annihilation of dislocation density. A duplex microstructure of ferrite 60% and austenite 40%was observed in the X-Ray Diffraction and etched metallography of the HIP-treated samples from a purely ferritic microstructure prior to the HIP treatment. With the evolution of austenite phase, the HIP-treated samples recorded a decrease in Ultimate Tensile Strength, yield strength, and hardness in comparison with as-printed samples. The variation in the morphology of the evolved austenite grains in the HIP-treated samples was observed to have a significant effect on the elongation. With a reduction in porosity and the evolution of the austenite phase, the HIP-treated samples showed a higher corrosion resistance in comparison with the as-printed samples.

Keywords

• L-PBF
• 25Cr7Ni stainless steel
• hot isostatic pressing
• corrosion properties